髓腔内压对树脂水门汀与牙本质粘接强度的影响

潘怡湘1,李秀花2,田福聪3,王晓燕1,∆()   

  1. 1. 北京大学口腔医学院·口腔医院,牙体牙髓科 国家口腔疾病临床医学研究中心 口腔数字化医疗技术和材料国家工程实验室 口腔数字医学北京市重点实验室, 北京 100081;
    2. 北京大学口腔医学院·口腔医院第五门诊部, 北京 100020;
  • 出版日期:2019-04-18 发布日期:2019-04-26
  • 通讯作者: 王晓燕 E-mail:wangxiaoyan@pkuss.bjmu.edu.cn

Effect of intrapulpal pressure on the bonding strength of resin cement to dentin

Yi-xiang PAN1,Xiu-hua LI2,Fu-cong TIAN3,Xiao-yan WANG1,∆()   

  1. 1. Department of Cariology and Endodontology, Peking University School and Hospital of Stomatology & National Clinical Research Center for Oral Diseases & National Engineering Laboratory for Digital and Material Technology of Stomatology & Beijing Key Laboratory of Digital Stomatology, Beijing 100081, China;
    2. Fifth Clinical Division, Peking University School and Hospital of Stomatology, Beijing 100020, China
  • Online:2019-04-18 Published:2019-04-26
  • Contact: Xiao-yan WANG E-mail:wangxiaoyan@pkuss.bjmu.edu.cn

RICH HTML

 7   

PDF (PC)

140

摘要：

目的: 评价髓腔内压条件对树脂水门汀与牙本质微拉伸粘接强度的影响。方法: 选择新拔除的人无龋第三磨牙30颗分成2组,去除咬合面釉质制备牙本质平面,选取剩余牙本质厚度为0.5~2.5 mm的牙本质试样,在有染料的髓腔内压条件下,观察牙本质表面与牙面处理剂Single Bond Universal(SBU)固化后表面在即刻、5 min、30 min、2 h的染料渗透情况。保持最小剩余牙本质厚度为(1.0±0.1) mm,分别在有或无髓腔内压条件(15或0 cmH2O,1 cmH2O=0.098 kPa)下维持30 min,使用SBU并光照固化,然后使用模具在牙本质表面堆塑RelyX Ultimate(RLX)树脂水门汀(直径10 mm,高4 mm),制备牙本质-树脂水门汀粘接试样。试样在37 ℃蒸馏水中储存24 h后,将牙本质-树脂水门汀试样垂直于粘接界面切割形成横截面积为0.9 mm×0.9 mm条状试样,使用微拉伸测试仪测试计算其粘接强度(两独立样本t检验,双侧检验水平α=0.05),用扫描电镜观察统计试样断裂类型(Fisher精确检验,双侧检验水平α=0.05)。将牙本质-树脂水门汀试样垂直粘接界面做切片,厚度0.8 mm,扫描电镜下观察粘接界面形貌。结果: 在髓腔内压条件下,随时间延长,粘接表面染料渗出增加。有髓腔内压时和无髓腔内压时RLX与牙本质微拉伸粘接强度分别为:(26.26±9.78) MPa和(28.70±9.09) MPa,两者差异无统计学意义(P>0.05)。两组试样断裂类型无明显差异(P>0.05),都以混合断裂为主。两组试样粘接界面可见4~8 μm指状树脂突,分布及长短较均匀,形貌无明显差异。结论: SBU预处理牙本质后,髓腔内压不影响树脂水门汀RLX的即刻牙本质粘接强度。

关键词: 树脂水门汀, 髓腔内压, 牙本质, 拉伸强度

Abstract:

Objective: To evaluate the effect of intrapulpal pressure simulation on the micro-tensile bond strength (μTBS) of resin cement to dentin.Methods: Thirty extracted human third molars were selected. Occlusal enamel was removed to expose dentine surface and teeth with residual dentin thickness of 0.5-2.5 mm were selected. Dye permeation through dentin tubules with or without intrapulpal pressure (IPP) simulation, or after Single Bond Universal (SBU) application on dentin surface with IPP simulation were observed at the end of 0 min, 5 min, 30 min and 2 h. The teeth with residual dentin thickness of (1.0±0.1) mm were divided into 2 groups with IPP simulation of 15 or 0 cmH2O (1 cmH2O=0.098 kPa), which was maintained for 30 min before bonding procedure. SBU was applied on the dentin surface and light cured, then RelyX Ultimate (RLX) cement was heaped on the dentin surface (diameter=10 mm, height=4 mm) and light-cured. After the dentin-resin cement samples were stored in distilled water for 24 h at 37 ℃, the samples were cut into beams with cross sectional area of 0.9 mm×0.9 mm for μTSB testing (n=100). The data were analyzed with two independent samples t-test (α=0.05). The fracture mode was observed using scanning electron microscopy (SEM). The results were analyzed with Fisher exact test (α=0.05). The rest of dentin-resin cement samples (five samples for each group) were cut perpendicular to the bonding interface and the morphology of the bonding interface was observed using SEM.Results: The dye permeation through dentin tubules with IPP simulation was faster than those without IPP simulation. The μTSB of RLX to dentin with and without IPP simulation were (26.26±9.78) MPa and (28.70±9.0) MPa, respectively. The most frequent fracture mode was mixed-fracture mode. There was no significant difference between the two groups for neither bond strength nor fracture types distribution (P>0.05). Regarding the morphology of dentin-resin cement bonding interface, both groups showed 4-8 μm finger-like resin tags.Conclusion: With SBU pretreatment, the IPP simulation had no influence on the immediate bond strength of RLX to dentin.

Key words: Resin cements, Intrapulpal pressure, Dentin, Tensile strength

中图分类号: 

  • R783.1

表1

实验用粘接剂和树脂水门汀的组成与使用方法"

Materials Composition Application procedures pH
SBU (3M ESPE, USA) 10-MDP,Bis-GMA,dimethacrylate resins,HEMA,vitrebond copolymer, silane, ethanol, water, filler, initiators 1. Apply the adhesive to the dentin surface and rub it in for 20 s
2. Direct a gentle stream of air over the liquid for about 10 s until it no longer moves
3. Light cure for 10 s		 2.7
RLX (3M ESPE, USA) Base paste: methacrylate monomers, radiopaque silanated fillers, initiator components, stabilizers, rheological additives
Catalyst paste: methacrylate monomers, radiopaque alkaline fillers, initiator components, stabilizers, pigments, rheological additives, fluorescence dye		 1. Automix
2. Place on the dentin surface
3. Light cure for 40 s/surf

图1

模拟髓室压力装置示意图"

图2

髓腔内压条件下牙本质面染料渗透情况"

表2

髓腔内压条件对RLX树脂水门汀微拉伸粘接强度及断裂类型统计(n=100)"

Groups μTBS/MPa, x?±s Fracture modes/%
Cohesive in RLX failure Mixed failure Interfacial failure Cohesive in dentin failure
SBU+RLX with IPP 26.26±9.78 9 84 0 7
SBU+RLX without IPP 28.70±9.09 9 83 0 8

图3

牙本质-树脂水门汀粘接界面扫描电镜图"

[1] 林红 . 口腔材料学[M]. 2版. 北京: 北京大学医学出版社, 2013: 193-196.
[2] Kawano S, Fu J, Saikaew P , et al. Microtensile bond strength of a newly developed resin cement to dentin[J]. Dent Mater J, 2015,34(1):61-69.
doi: 10.4012/dmj.2014-122
[3] André CB, Aguiar TR, Ayres AP , et al. Bond strength of self-adhesive resin cements to dry and moist dentin[J]. Braz Oral Res, 2013,27(5):389-395.
doi: 10.1590/S1806-83242013000500002
[4] Cardoso MV, Moretto SG, Carvalho RC , et al. Influence of intrapulpal pressure simulation on the bond strength of adhesive systems to dentin[J]. Braz Oral Res, 2008,22(2):170-175.
doi: 10.1590/S1806-83242008000200013
[5] Feitosa VP, Gotti VB, Grohmann CV , et al. Two methods to si-mulate intrapulpal pressure: effects upon bonding performance of self-etch adhesives[J]. Int Endod J, 2014,47(9):819-826.
doi: 10.1111/iej.2014.47.issue-9
[6] Flury S, Peutzfeldt A, Schmidlin PR , et al. Exposed dentin: Influence of cleaning procedures and simulated pulpal pressure on bond strength of a universal adhesive system[J]. PLoS One, 2017,12(1):e169680.
[7] Hiraishi N, Yiu CK, King NM , et al. Effect of pulpal pressure on the microtensile bond strength of luting resin cements to human dentin[J]. Dent Mater, 2009,25(1):58-66.
doi: 10.1016/j.dental.2008.05.005
[8] Mazzitilli C, Monticelli F, Toledano M , et al. Dentin treatment effects on the bonding performance of self-adhesive resin cements[J]. Eur J Oral Sci, 2010,118(1):80-86.
doi: 10.1111/eos.2010.118.issue-1
[9] Mohamed MF, El Deeb HA, Gomaa IE , et al. Bond durability of different resin cements to caries-affected dentin under simulated intrapulpal pressure[J]. Oper Dent, 2015,40(3):293-303.
doi: 10.2341/14-035-L
[10] Moosavi H, Hariri I, Sadr A , et al. Effects of curing mode and moisture on nanoindentation mechanical properties and bonding of a self-adhesive resin cement to pulp chamber floor[J]. Dent Mater, 2013,29(6):708-717.
doi: 10.1016/j.dental.2013.03.020
[11] Souza GD, Braga RR, Cesar PF , et al. Correlation between clinical performance and degree of conversion of resin cements: a lite-rature review[J]. J Appl Oral Sci, 2015,23(4):358-368.
doi: 10.1590/1678-775720140524
[12] 傅昭然, 田福聪, 张路 , 等. 通用型粘接剂对双固化树脂水门汀牙本质粘接强度的影响[J]. 北京大学学报(医学版), 2017,49(1):101-104.
[13] Bakry AS, Nakajima M, Otsuki M , et al. Effect of Er:YAG laser on dentin bonding durability under simulated pulpal pressure[J]. J Adhes Dent, 2009,11(5):361-368.
[14] Krejci I, Häusler T, Sägesser , et al. New adhesives in class V restorations under combined load and simulated dentinal fluid[J]. Dent Mater, 1994,10(5):331-335.
doi: 10.1016/0109-5641(94)90042-6
[15] 高学军, 岳林 . 牙体牙髓病学[M]. 2版. 北京: 北京大学医学出版社, 2013: 31-32.
[16] Shaymma M . Durability of solvent-free one-step self-etch adhesive under simulated intrapulpal pressure[J]. J Clin Exp Dent, 2015,7(4):e466-e470.
[17] Acar O, Erkut S, Lakshmipathy M . Surface detail reproduction under simulated pulpal pressure: a 3-dimensional optical profilometer and scanning electron microscopy evaluation[J]. J Prosthet Dent, 2012,108(2):102-113.
doi: 10.1016/S0022-3913(12)60116-4
[18] 关天燕, 张彦博, 陈国常 , 等. 模拟髓室压力对两种自酸蚀粘接剂牙本质粘接强度的影响[J]. 口腔疾病防治, 2011,19(10):516-519.
[19] Tay FR, Gwinnett JA, Wei SH . The overwet phenomenon in two-component acetone-based primers containing aryl amine and carboxylic acid monomers[J]. Dent Mater, 1997,13(2):118-127.
doi: 10.1016/S0109-5641(97)80021-8
[20] Wagner A, Wendler M, Petschelt A , et al. Bonding performance of universal adhesives in different etching modes[J]. J Dent, 2014,42(7):800-807.
doi: 10.1016/j.jdent.2014.04.012
[21] Kim HJ, Bagheri R, Kim YK , et al. Influence of curing mode on the surface energy and sorption/solubility of dental self-adhesive resin cements[J]. Materials (Basel), 2017,10(2):129-130.
doi: 10.3390/ma10020129
[22] Mobarak EH, El-Deeb HA, Yousry MM . Influence of different intrapulpal pressure simulation liquids on the microtensile bond strength of adhesive systems to dentin[J]. J Adhes Dent, 2013,15(6):519-526.
[1] 马欣蓉,朱晓鸣,李静,李德利,李和平,谭建国. 新型大气压冷等离子体射流处理对牙本质胶原纤维交联化的影响[J]. 北京大学学报（医学版）, 2022, 54(1): 83-88.
[2] 骆池怡,彭楚芳,杨媛,秦满,王媛媛. 3种自酸蚀粘接系统和轻度唾液污染对乳牙釉质及牙本质粘接耐久性的影响[J]. 北京大学学报（医学版）, 2021, 53(1): 46-53.
[3] 陈文新,包旭东,岳林. 固化方式对树脂水门汀氧阻聚层形成的影响[J]. 北京大学学报（医学版）, 2020, 52(6): 1117-1123.
[4] 李秋菊,宫玮玉,董艳梅. 生物活性玻璃预处理对牙本质粘接界面耐久性的影响[J]. 北京大学学报（医学版）, 2020, 52(5): 931-937.
[5] 李芳,刘洋,刘浩辰,冯海兰. 乳光牙本质患者的基因变异分析及患牙的组织学观察[J]. 北京大学学报(医学版), 2018, 50(4): 666-671.
[6] 廖宇，刘晓强，陈立，周建锋，谭建国. 不同表面处理方法对氧化锆与树脂水门汀粘接强度的影响[J]. 北京大学学报(医学版), 2018, 50(1): 53-57.
[7] 臧海玲，王月，梁宇红. 有机溶剂对牙本质表面残留根管封闭剂的清除效果[J]. 北京大学学报(医学版), 2018, 50(1): 63-68.
[8] 贾维茜，赵玉鸣，葛立宏. 人重组转化生长因子β1促进牙髓干细胞的增殖和矿化[J]. 北京大学学报(医学版), 2017, 49(4): 680-681.
[9] 李皓，刘玉华，罗志强. 生物活性玻璃用于缓解活髓牙全冠预备后敏感的效果评价[J]. 北京大学学报(医学版), 2017, 49(4): 709-713.
[10] 信义，王赛楠，崔彩云，董艳梅. 生物活性玻璃和牙本质浸提蛋白对人牙髓细胞的作用[J]. 北京大学学报(医学版), 2017, 49(2): 331-336.
[11] 王月，梁宇红. 次氯酸钠溶液表面处理对牙本质粘接强度的影响[J]. 北京大学学报(医学版), 2017, 49(1): 105-109.
[12] 傅昭然，田福聪，张路，韩冰，王晓燕. 通用型粘接剂对双固化树脂水门汀牙本质粘接强度的影响[J]. 北京大学学报(医学版), 2017, 49(1): 101-104.
[13] 郭惠杰，高承志， 林斐，刘伟，岳林. 唾液污染对复合树脂间粘接强度的影响[J]. 北京大学学报(医学版), 2017, 49(1): 96-100.
[14] 郭怡丹，张笋. Er:YAG激光用于比格犬牙髓切断术[J]. 北京大学学报(医学版), 2016, 48(4): 714-719.
[15] 张路， 袁重阳， 田福聪， 王晓燕， 高学军. 自酸蚀粘接剂系统对变形链球菌的抑制作用[J]. 北京大学学报(医学版), 2016, 48(1): 57-62.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
[1] 张三. 中文标题测试[J]. 北京大学学报（医学版）, 2010, 42(1): 1 -10 .
[2] 赵磊, 王天龙 . 右心室舒张末期容量监测用于肝移植术中容量管理的临床研究[J]. 北京大学学报（医学版）, 2009, 41(2): 188 -191 .
[3] 万有, , 韩济生, John E. Pintar. 孤啡肽基因敲除小鼠电针镇痛作用增强[J]. 北京大学学报（医学版）, 2009, 41(3): 376 -379 .
[4] 张燕, 韩志慧, 钟延丰, 王盛兰, 李玲玲, 郑丹枫. 骨骼肌活组织检查病理诊断技术的改进及应用[J]. 北京大学学报（医学版）, 2009, 41(4): 459 -462 .
[5] 赵奇, 薛世华, 刘志勇, 吴凌云. 同向施压测定自酸蚀与全酸蚀粘接系统粘接强度[J]. 北京大学学报（医学版）, 2010, 42(1): 82 -84 .
[6] 李岳玲, 钱秋瑾, 王玉凤. 儿童注意缺陷多动障碍成人期预后及其预测因素[J]. 北京大学学报（医学版）, 2007, 39(3): 337 -340 .
[7] . 书讯[J]. 北京大学学报（医学版）, 2007, 39(3): 225 -328 .
[8] 牟向东, 王广发, 刁小莉, 阙呈立. 肺黏膜相关淋巴组织型边缘区B细胞淋巴瘤一例[J]. 北京大学学报（医学版）, 2007, 39(4): 346 -350 .
[9] 韩金涛, 赵军, 栾景源, 张龙. 多发结核性腹主动脉瘤一例[J]. 北京大学学报（医学版）, 2007, 39(4): 361 -364 .
[10] 燕太强, 杨荣利, 郭卫, 沈丹华. 胫骨平滑肌肉瘤伴全身多发骨转移一例[J]. 北京大学学报（医学版）, 2007, 39(4): 369 -373 .
ISSN 1671-167X
CN 11-4691/R
主管单位：中华人民共和国教育部
主办单位：北京大学
地址： 北京市海淀区学院路38号 北京大学医学部 《北京大学学报（医学版）》
邮编：100191
电话：010-82801551
Email： xbbjb2@bjmu.edu.cn

《北京大学学报（医学版）》
微信公众号
版权所有 © 2018 《北京大学学报（医学版）》编辑部