Effect of intrapulpal pressure on the bonding strength of resin cement to dentin
Online published: 2019-04-26
Objective: To evaluate the effect of intrapulpal pressure simulation on the micro-tensile bond strength (μTBS) of resin cement to dentin.Methods: Thirty extracted human third molars were selected. Occlusal enamel was removed to expose dentine surface and teeth with residual dentin thickness of 0.5-2.5 mm were selected. Dye permeation through dentin tubules with or without intrapulpal pressure (IPP) simulation, or after Single Bond Universal (SBU) application on dentin surface with IPP simulation were observed at the end of 0 min, 5 min, 30 min and 2 h. The teeth with residual dentin thickness of (1.0±0.1) mm were divided into 2 groups with IPP simulation of 15 or 0 cmH2O (1 cmH2O=0.098 kPa), which was maintained for 30 min before bonding procedure. SBU was applied on the dentin surface and light cured, then RelyX Ultimate (RLX) cement was heaped on the dentin surface (diameter=10 mm, height=4 mm) and light-cured. After the dentin-resin cement samples were stored in distilled water for 24 h at 37 ℃, the samples were cut into beams with cross sectional area of 0.9 mm×0.9 mm for μTSB testing (n=100). The data were analyzed with two independent samples t-test (α=0.05). The fracture mode was observed using scanning electron microscopy (SEM). The results were analyzed with Fisher exact test (α=0.05). The rest of dentin-resin cement samples (five samples for each group) were cut perpendicular to the bonding interface and the morphology of the bonding interface was observed using SEM.Results: The dye permeation through dentin tubules with IPP simulation was faster than those without IPP simulation. The μTSB of RLX to dentin with and without IPP simulation were (26.26±9.78) MPa and (28.70±9.0) MPa, respectively. The most frequent fracture mode was mixed-fracture mode. There was no significant difference between the two groups for neither bond strength nor fracture types distribution (P>0.05). Regarding the morphology of dentin-resin cement bonding interface, both groups showed 4-8 μm finger-like resin tags.Conclusion: With SBU pretreatment, the IPP simulation had no influence on the immediate bond strength of RLX to dentin.
Key words： Resin cements; Intrapulpal pressure; Dentin; Tensile strength
Yi-xiang PAN , Xiu-hua LI , Fu-cong TIAN , Xiao-yan WANG . Effect of intrapulpal pressure on the bonding strength of resin cement to dentin[J]. Journal of Peking University(Health Sciences), 2019 , 51(2) : 321 -326 . DOI: 10.19723/j.issn.1671-167X.2019.02.023
| [1] | 林红 . 口腔材料学[M]. 2版. 北京: 北京大学医学出版社, 2013: 193-196. |
| [2] | Kawano S, Fu J, Saikaew P , et al. Microtensile bond strength of a newly developed resin cement to dentin[J]. Dent Mater J, 2015,34(1):61-69. |
| [3] | André CB, Aguiar TR, Ayres AP , et al. Bond strength of self-adhesive resin cements to dry and moist dentin[J]. Braz Oral Res, 2013,27(5):389-395. |
| [4] | Cardoso MV, Moretto SG, Carvalho RC , et al. Influence of intrapulpal pressure simulation on the bond strength of adhesive systems to dentin[J]. Braz Oral Res, 2008,22(2):170-175. |
| [5] | Feitosa VP, Gotti VB, Grohmann CV , et al. Two methods to si-mulate intrapulpal pressure: effects upon bonding performance of self-etch adhesives[J]. Int Endod J, 2014,47(9):819-826. |
| [6] | Flury S, Peutzfeldt A, Schmidlin PR , et al. Exposed dentin: Influence of cleaning procedures and simulated pulpal pressure on bond strength of a universal adhesive system[J]. PLoS One, 2017,12(1):e169680. |
| [7] | Hiraishi N, Yiu CK, King NM , et al. Effect of pulpal pressure on the microtensile bond strength of luting resin cements to human dentin[J]. Dent Mater, 2009,25(1):58-66. |
| [8] | Mazzitilli C, Monticelli F, Toledano M , et al. Dentin treatment effects on the bonding performance of self-adhesive resin cements[J]. Eur J Oral Sci, 2010,118(1):80-86. |
| [9] | Mohamed MF, El Deeb HA, Gomaa IE , et al. Bond durability of different resin cements to caries-affected dentin under simulated intrapulpal pressure[J]. Oper Dent, 2015,40(3):293-303. |
| [10] | Moosavi H, Hariri I, Sadr A , et al. Effects of curing mode and moisture on nanoindentation mechanical properties and bonding of a self-adhesive resin cement to pulp chamber floor[J]. Dent Mater, 2013,29(6):708-717. |
| [11] | Souza GD, Braga RR, Cesar PF , et al. Correlation between clinical performance and degree of conversion of resin cements: a lite-rature review[J]. J Appl Oral Sci, 2015,23(4):358-368. |
| [12] | 傅昭然, 田福聪, 张路 , 等. 通用型粘接剂对双固化树脂水门汀牙本质粘接强度的影响[J]. 北京大学学报(医学版), 2017,49(1):101-104. |
| [13] | Bakry AS, Nakajima M, Otsuki M , et al. Effect of Er:YAG laser on dentin bonding durability under simulated pulpal pressure[J]. J Adhes Dent, 2009,11(5):361-368. |
| [14] | Krejci I, H?usler T, S?gesser , et al. New adhesives in class V restorations under combined load and simulated dentinal fluid[J]. Dent Mater, 1994,10(5):331-335. |
| [15] | 高学军, 岳林 . 牙体牙髓病学[M]. 2版. 北京: 北京大学医学出版社, 2013: 31-32. |
| [16] | Shaymma M . Durability of solvent-free one-step self-etch adhesive under simulated intrapulpal pressure[J]. J Clin Exp Dent, 2015,7(4):e466-e470. |
| [17] | Acar O, Erkut S, Lakshmipathy M . Surface detail reproduction under simulated pulpal pressure: a 3-dimensional optical profilometer and scanning electron microscopy evaluation[J]. J Prosthet Dent, 2012,108(2):102-113. |
| [18] | 关天燕, 张彦博, 陈国常 , 等. 模拟髓室压力对两种自酸蚀粘接剂牙本质粘接强度的影响[J]. 口腔疾病防治, 2011,19(10):516-519. |
| [19] | Tay FR, Gwinnett JA, Wei SH . The overwet phenomenon in two-component acetone-based primers containing aryl amine and carboxylic acid monomers[J]. Dent Mater, 1997,13(2):118-127. |
| [20] | Wagner A, Wendler M, Petschelt A , et al. Bonding performance of universal adhesives in different etching modes[J]. J Dent, 2014,42(7):800-807. |
| [21] | Kim HJ, Bagheri R, Kim YK , et al. Influence of curing mode on the surface energy and sorption/solubility of dental self-adhesive resin cements[J]. Materials (Basel), 2017,10(2):129-130. |
| [22] | Mobarak EH, El-Deeb HA, Yousry MM . Influence of different intrapulpal pressure simulation liquids on the microtensile bond strength of adhesive systems to dentin[J]. J Adhes Dent, 2013,15(6):519-526. |
/
| 〈 |
|
〉 |