对比切削与胶态成型工艺制作的氧化锆陶瓷的透光性与遮色效果

崔新悦1,佟岱1,2,王新知1△,沈志坚3   

  1. (北京大学口腔医学院·口腔医院, 1. 修复科, 2. 义齿加工中心口腔数字化医疗技术和材料国家工程实验室口腔数字医学北京市重点实验室, 北京100081; 3. Department of Materials and Environmental Chemistry, Arrhenius Laboratory, Stockholm University, S-106 91 Stockholm, Sweden)
  • 出版日期:2018-02-18 发布日期:2018-02-18
  • 通讯作者: 王新知 E-mail: xinzwang@sina.com

Comparison of the translucency and color masking effect of the zirconia ceramics made by milling and gel deposition

CUI Xin-yue1, TONG Dai1,2, WANG Xin-zhi1△, SHEN Zhi-jian3   

  1. (1. Department of Prosthodontics, 2. Dental Laboratory, Peking University School and Hospital of Stomatology & National Engineering Laboratory for Digital and Material Technology of Stomatology & Beijing Key Laboratory of Digital Stomatology, Beijing 100081, China; 3. Department of Materials and Environmental Chemistry, Arrhenius Laboratory, Stockholm University, S106 91 Stockholm, Sweden)
  • Online:2018-02-18 Published:2018-02-18
  • Contact: WANG Xin-zhi E-mail: xinzwang@sina.com

摘要: 目的:利用切削素烧瓷块法与三维(three dimensional,3D)胶态成型法制作遮色效果不同的3种氧化锆陶瓷,对比其在不同厚度下的透光性及对异色离体牙的遮色效果,为临床口腔修复提供材料选择依据。方法:制备90片直径14 mm的A2色氧化锆圆盘试件,分成3组(n=30):(1)CZ组,采用计算机辅助设计(computer aided design,CAD)/计算机辅助制造(computer aided manufacturing,CAM)切削素烧瓷块法;(2)NZW组,采用3D胶态成型法,试件内表面无多孔遮色层;(3)NZY组,采用3D胶态成型法,试件内表面有多孔遮色层。3组试件根据厚度0.6 mm、1.0 mm、1.5 mm再分成3个亚组(n=10)。选用因牙周病拔除的中、重度异色前牙10颗,唇面打磨成大于 6 mm2×6 mm2的平面。暗盒中用Crystaleye比色仪在黑、白背景下分别测量9组试件的色度值(CIE1976L*a*b*),计算透光性[半透性参数(translucency parameter, TP)]。将每组试件与牙齿唇面依次粘接并测量色度值。选标准比色片A2中1/3色度值作为对照,计算试件粘接后同对照色的色差ΔE。以One-way ANOVA和Bonferroni法对数据进行统计分析。结果:(1)3组氧化锆试件在0.6 mm、1.0 mm、1.5 mm 厚度下的TP值分别为:CZ组14.09、12.31和10.45,NZW组19.84、16.54和12.44,NZY组14.81、13.16和11.92。每组试件的3个亚组间透光性均显示为0.6 mm组>1.0 mm组>1.5 mm组,厚度相同的亚组间透光性均显示为NZW组>NZY组>CZ组。(2)3组氧化锆试件粘接后在0.6 mm、1.0 mm、1.5 mm厚度下与对照色的色差ΔE分别为:CZ组10.77、9.94和8.50,NZW组6.84、5.89和5.29,NZY组4.16、3.92和3.67。每组试件的3个亚组间色差值均显示为0.6 mm组>1.0 mm组>1.5 mm组,厚度相同的亚组间色差值均显示为CZ组>NZW组>NZY组。结论:3种氧化锆试件在厚度相同的情况下,透光性均为3D胶态成型技术制作的内表面无遮色处理组试件最好,而遮色效果均为3D胶态成型技术制作的内表面有遮色处理组试件最好,且其厚度在0.6 mm时即可获得较好的遮色效果。

关键词: 氧化锆, 陶瓷, 颜色, 牙科, 美学

Abstract: Objective: Three kinds of zirconia specimens were made respectively by milling of the pri-sintered blocks and by three dimensional (3D) gel deposition for in vitro evaluation of their optical translucency under three different thicknesses and their color masking effect on discolored teeth. The study aims for establishing the principle for guiding the materials selection in clinical practice. Methods: Ninety A2-colored zirconia disc specimens with diameter of 14 mm were prepared and were divided into three groups (n=30). (1) Group CZ, by milling of the pre-sintered blanks; (2) Group NZW, by 3D gel deposition, without a color masking opaque inner layer; (3) Group NZY, by 3D gel deposition, with a color masking opaque inner layer. Furthermore, each group was divided into three sub-groups (n=10) according to the sample thickness, i.e., 0.6, 1.0 and 1.5 mm, respectively. The maxillary anterior teeth with severe discoloration, extracted owing to periodontal disease, were collected and embedded. By gentle gridding and polishing a plane, larger than 6 mm2×6 mm2, was generated on the labial surface of each tooth. Chromatic values(CIE1976-L*a*b*) of the zirconia samples in the nine subgroups were measured by the spectrophotometer Crystaleye in front of the black or white background in a cassette, and the translucency parameter (TP) values were calculated for each sample. Thereafter the zirconia specimens were bonded onto the labial surface of the polished teeth for measuring the chromatic values, using the chromatic value of the medium 1/3 of the standardized Vita A2 as a control. The color aberration ΔE between each zirconia specimen and the control value was calculated, respectively. The results were statistically analyzed by One-way ANOVA and Bonferroni. Results: (1) The optical transparency of the three kinds of zirconia disc specimens with the thickness of 0.6, 1.0 and 1.5 mm was 14.09, 12.31 and 10.45 for group CZ;19.84, 16.54 and 12.44 for group NZW;14.81, 13.16 and 11.92 for group NZY. In each group, the degree of optical transparency of the specimens showed a clear tendency as in the sub-group 0.6 mm >1.0 mm >1.5 mm. The TP value of the specimens in the three groups with the same thickness showed a tendency of the group NZW >group NZY >group CZ. (2) After bonding onto the polished labial surface of the teeth, the color aberration ΔE of the specimens with the thickness of 0.6, 1.0 and 1.5 mm was calculated to be 10.77, 9.94 and 8.50 for group CZ; 6.84, 5.89 and 5.29 for group NZW; 4.16, 3.92 and 3.67 for group NZY. In each group, the color aberration of the specimens showed a clear tendency as in the sub-group 0.6 mm >1.0 mm >1.5 mm; the color aberration of the three groups with the same thickness was in the order of the group CZ >group NZW >group NZY. Conclusion: In all the specimen groups with a fixed specimen thickness, the optical translucency of the specimen was the highest in group NZW made by 3D gel deposition, and the best color masking effect was obtained in specimens with a color masking opaque inner layer in group NZY, where a thickness of 0.6 mm was sufficient enough for obtaining the ideal color masking effect.

Key words: Zirconia, Ceramics, Color, Esthetics, dental

中图分类号: 

  • R783.1
[1] 吕梁,张铭津,温奧楠,赵一姣,王勇,李晶,杨庚辰,柳大为. 应用三维软组织空间线角模板法评价颏部对称性[J]. 北京大学学报(医学版), 2024, 56(1): 106-110.
[2] 郑佳佳,杨雪,温泉,付元,邵校,丁美丽. 生物活性陶瓷iRoot BP Plus®在儿童年轻恒前牙复杂冠折牙髓切断术中的应用[J]. 北京大学学报(医学版), 2024, 56(1): 179-184.
[3] 丁茜,李文锦,孙丰博,谷景华,林元华,张磊. 表面处理对氧化钇和氧化镁稳定的氧化锆种植体晶相及断裂强度的影响[J]. 北京大学学报(医学版), 2023, 55(4): 721-728.
[4] 雍颹,钱锟,朱文昊,赵晓一,刘畅,潘洁. 成年恒牙牙髓切断后牙髓钙化的X线片评价[J]. 北京大学学报(医学版), 2023, 55(1): 88-93.
[5] 李伟伟,陈虎,王勇,孙玉春. 氧化锆陶瓷表面硅锂喷涂层的摩擦磨损性能[J]. 北京大学学报(医学版), 2023, 55(1): 94-100.
[6] 王爽,彭楚芳,刘鹤. 新型生物陶瓷材料用于乳磨牙牙髓切断术的临床疗效[J]. 北京大学学报(医学版), 2022, 54(6): 1196-1201.
[7] 刘云松,周倜,叶红强. 前牙美学修复的整体策略及细节剖析[J]. 北京大学学报(医学版), 2022, 54(1): 1-6.
[8] 钱锟,潘洁,朱文昊,赵晓一,刘畅,雍颹. 两种硅酸钙类材料用于成熟恒牙牙髓切断术的临床效果[J]. 北京大学学报(医学版), 2022, 54(1): 113-118.
[9] 孙菲,李思琪,危伊萍,钟金晟,王翠,胡文杰. 种植体周病非手术治疗中联合应用甘氨酸粉喷砂的临床效果评价[J]. 北京大学学报(医学版), 2022, 54(1): 119-125.
[10] 李怡,王丽瑜,刘晓强,周倜,吕季喆,谭建国. 不同材料及厚度椅旁CAD/CAM瓷贴面的边缘特征[J]. 北京大学学报(医学版), 2022, 54(1): 140-145.
[11] 王鹃,尉华杰,孙井德,邱立新. 预成刚性连接杆用于无牙颌种植即刻印模制取的应用评价[J]. 北京大学学报(医学版), 2022, 54(1): 187-192.
[12] 邱淑婷,朱玉佳,王时敏,王飞龙,叶红强,赵一姣,刘云松,王勇,周永胜. 姿势微笑位口唇对称参考平面的数字化构建及初步应用验证[J]. 北京大学学报(医学版), 2022, 54(1): 193-199.
[13] 王铮,丁茜,高远,马全诠,张磊,葛兮源,孙玉春,谢秋菲. 氧化锆多孔表面显微形貌对成骨细胞增殖及分化的影响[J]. 北京大学学报(医学版), 2022, 54(1): 31-39.
[14] 徐欣然,霍芃呈,和璐,孟焕新,朱筠轩,靳东思奇. 伴与不伴糖尿病的牙周炎患者牙周基础治疗的疗效比较及其与白细胞水平的相关分析[J]. 北京大学学报(医学版), 2022, 54(1): 48-53.
[15] 李智,徐永祥,包旭东,王晓燕. 垫底树脂和固位深度对树脂基纳米陶瓷髓腔固位冠修复磨牙抗折性能的影响[J]. 北京大学学报(医学版), 2022, 54(1): 95-99.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!