计算机辅助设计与制作的一体化氧化锆全瓷桩核抗折力的体外对比实验

北京大学学报（医学版） ›› 2014, Vol. 46 ›› Issue (1): 81-85.

计算机辅助设计与制作的一体化氧化锆全瓷桩核抗折力的体外对比实验

周团锋1，2*，张相皞3*，王新知1△

（1.北京大学口腔医学院·口腔医院修复科，北京100081； 2.北京大学口腔医学院·口腔医院第一门诊部，北京100034； 3.北京大学口腔医学院·口腔医院第二门诊部，北京100101）

出版日期:2014-02-18 发布日期:2014-02-18

Fracture resistance of teeth restored with onepiece computer aided design and manufacture zirconia posts and cores: an in vitro study

ZHOU Tuan-feng1,2*,ZHANG Xiang-hao3*,WANG Xin-zhi1△

(1. Department of Prosthodontics,Peking University School and Hospital of Stomatology, Beijing 100081,China; 2. First Clinical Division,PekingUnivesity School and Hospital of Stomatology, Beijing 100034,China; 3. Second Clinical Division,Peking University School and Hospital of Stomatology,Beijing 100101,China)

Online:2014-02-18 Published:2014-02-18

摘要/Abstract

摘要： 目的：比较预成氧化锆全瓷桩、计算机辅助设计与制作的（computer aided design and computer aided manufacture， CAD/CAM）一体化氧化锆全瓷桩核和天然离体牙的抗折力大小，为临床桩核冠修复材料和方式的选择提供一定的参考。方法：采用36颗离体完整的上颌中切牙，随机分为预成氧化锆全瓷桩铸瓷核金属全冠修复、CAD/CAM一体化氧化锆全瓷桩核金属全冠修复和完整离体牙3组，每组12颗。在力学万能实验机上，在冠切缘下2.0 mm，沿牙体长轴135°，以1 mm/min的速度加载，测量3组抗折力的大小。结果：完整离体牙组的抗折力最大［(736.33±82.91) N］，CAD/CAM一体化氧化锆全瓷桩核组次之［（423.83 ± 54.58） N］，预成氧化锆全瓷桩铸瓷核组最小［（311.75 ± 70.12）N］，单因素方差分析差异有统计学意义（P<0.001）。结论：CAD/CAM一体化氧化锆全瓷桩核有较高的抗折能力，在前牙美学修复中的应用有一定优势。

关键词: 计算机辅助设计, 氧化锆, 牙应力分析, 桩核技术, 体外研究

Abstract: Objective：To compare the fracture resistance of endodontically-treated teeth restored with prefabricated zirconia posts or one-piece computer aided design and computer aided manufacture (CAD/CAM) zirconia posts and cores, and unrestored endodontically-treated teeth. Methods: Recently extracted human maxillary central incisors (n=36) were endodontically treated and divided into three groups (n=12 each): group 1 was restored with prefabricated zirconia posts (Comospost) and hot pressed ceramic cores; group 2 restored with one-piece CAD/CAM zirconia posts and cores; group 3 not restored. The teeth were fixed in a universal load-testing machine; a compressive load was applied at 135 degrees to the long axis of each tooth at a crosshead speed of 1 mm/min until fracture. One-way analysis of variance (Student-Newman-Keuls) was used to determine the significance of the differences in failure load between the groups.Results: The mean fracture loads were (311.75 ± 70.12) N, (423.83 ± 54.58) N and (736.33 ± 82.91) N, respectively. The unrestored teeth exhibited significantly higher fracture resistance than the two groups of restored teeth. The teeth restored with one-piece CAD/CAM zirconia posts and cores had higher fracture resistance than the teeth restored with prefabricated zirconia posts and hot pressed ceramic cores (P < 0.001). Conclusion: Within the limitations of this study, the root canal-treated teeth restored with one-piece CAD/CAM zirconia posts and cores had a significantly higher failure resistance than the teeth restored with prefabricated zirconia posts. One-piece CAD/CAM zirconia posts and cores can offer some advantages for esthetic prosthodontics.

Key words: Computer-aided design, Zirconium oxide, Dental stress analysis, Post and core technique, In vitro

周团锋，张相皞，王新知. 计算机辅助设计与制作的一体化氧化锆全瓷桩核抗折力的体外对比实验[J]. 北京大学学报（医学版）, 2014, 46(1): 81-85.

ZHOU Tuan-feng,ZHANG Xiang-hao,WANG Xin-zhi. Fracture resistance of teeth restored with onepiece computer aided design and manufacture zirconia posts and cores: an in vitro study[J]. Journal of Peking University(Health Sciences), 2014, 46(1): 81-85.

参考文献

相关文章 15

[1]	于录, 吴灵, 刘筱菁, 李自力. 基于数据库相似性检索的正颌外科手术规划技术流程可行性研究: 随机对照试验[J]. 北京大学学报（医学版）, 2026, 58(1): 145-152.
[2]	赵健霄, 丁茜, 李文锦, 马全诠, 兰一笑, 张磊, 韩建民. 多孔表面结构对立体光固化成型氧化锆疲劳强度的影响[J]. 北京大学学报（医学版）, 2025, 57(6): 1165-1173.
[3]	钱锟, 刘亦洪. 基于直接法和间接法数字印模制作的高嵌体适合性评价的体外研究[J]. 北京大学学报（医学版）, 2025, 57(3): 604-609.
[4]	马丽娟, 腾雍辉, 王勇, 赵一姣, 张馨月, 秦庆钊, 尹东. 乳牙缺失数字化丝圈间隙保持器的三维有限元分析[J]. 北京大学学报（医学版）, 2025, 57(2): 376-383.
[5]	徐心雨,吴灵,宋凤岐,李自力,张益,刘筱菁. 基于下颌运动轨迹的正颌外科术中下颌骨髁突定位方法及初步精度验证[J]. 北京大学学报（医学版）, 2024, 56(1): 57-65.
[6]	李穗,马雯洁,王时敏,丁茜,孙瑶,张磊. 上前牙种植单冠修复体切导的数字化设计正确度[J]. 北京大学学报（医学版）, 2024, 56(1): 81-87.
[7]	丁茜,李文锦,孙丰博,谷景华,林元华,张磊. 表面处理对氧化钇和氧化镁稳定的氧化锆种植体晶相及断裂强度的影响[J]. 北京大学学报（医学版）, 2023, 55(4): 721-728.
[8]	李伟伟,陈虎,王勇,孙玉春. 氧化锆陶瓷表面硅锂喷涂层的摩擦磨损性能[J]. 北京大学学报（医学版）, 2023, 55(1): 94-100.
[9]	罗昊,田福聪,王晓燕. 不同椅旁可切削修复材料序列抛光时间及表面粗糙度与光泽度的比较[J]. 北京大学学报（医学版）, 2022, 54(3): 565-571.
[10]	冯莎蔚,国慧,王勇,赵一姣,刘鹤. 乳牙数字化参考牙冠模型的初步构建[J]. 北京大学学报（医学版）, 2022, 54(2): 327-334.
[11]	李怡,王丽瑜,刘晓强,周倜,吕季喆,谭建国. 不同材料及厚度椅旁CAD/CAM瓷贴面的边缘特征[J]. 北京大学学报（医学版）, 2022, 54(1): 140-145.
[12]	邱淑婷,朱玉佳,王时敏,王飞龙,叶红强,赵一姣,刘云松,王勇,周永胜. 姿势微笑位口唇对称参考平面的数字化构建及初步应用验证[J]. 北京大学学报（医学版）, 2022, 54(1): 193-199.
[13]	王铮,丁茜,高远,马全诠,张磊,葛兮源,孙玉春,谢秋菲. 氧化锆多孔表面显微形貌对成骨细胞增殖及分化的影响[J]. 北京大学学报（医学版）, 2022, 54(1): 31-39.
[14]	李文锦,丁茜,原福松,孙丰博,郑剑桥,鲍蕊,张磊. 飞秒激光表面处理对氧化锆表面特征及弯曲强度的影响[J]. 北京大学学报（医学版）, 2021, 53(4): 770-775.
[15]	杨欣,李榕,叶红强,陈虎,王勇,周永胜,孙玉春. 不同刃状边缘补偿角度的两种氧化锆全瓷冠断裂强度的评价[J]. 北京大学学报（医学版）, 2021, 53(2): 402-405.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed