温度循环对自酸蚀粘接剂与牙本质粘接耐久性的影响

田福聪,王晓燕△, 高学军   

  1. (北京大学口腔医学院·口腔医院牙体牙髓科,北京100081)
  • 出版日期:2014-04-18 发布日期:2014-04-18

Influence of thermalcycling on bonding durability of selfetch adhesives with dentin

TIAN Fu-cong, WANG Xiao-yan△, GAO Xue-jun   

  1. (Department of Cariology and Endodontology, Peking University School and Hospital of Stomatology, Beijing 100081, China)
  • Online:2014-04-18 Published:2014-04-18

摘要: 目的:用温度循环的方法评价老化对一步法和两步法自酸蚀粘接剂与牙本质粘接耐久性的影响。方法:选择人离体磨牙42颗,制备浅层牙本质平面,随机分为6组,分别使用3种自酸蚀粘接剂: 两步法粘接剂Clearfil SE bond(SE),一步法粘接剂Adper Prompt(AP)和G-bond(GB),用复合树脂形成树脂冠。沿长轴纵向切割成1.0 mm×1.0 mm的条状,在粘接后24 h、温度循环(5 ℃~55 ℃)5 000次后测试微拉伸粘接强度及进行硝酸铵银渗漏实验观察界面纳米渗漏情况。粘接强度值采用单因素方差分析进行统计分析,界面渗漏情况在扫描电镜背散射模式下进行观察。结果:3种粘接剂微拉伸粘接强度分别为:SE粘接即刻(40.60±5.76) MPa,温度循环后(45.80±2.97) MPa;AP粘接即刻(19.06±1.50) MPa,温度循环后(12.62±2.10) MPa;GB粘接即刻(17.75±1.10) MPa,温度循环后(6.24±0.42) MPa。单因素方差分析显示粘接剂种类与温度循环对粘接强度均有显著影响(P<0.05),二者之间存在交互作用。温度循环后,AP与GB强度显著下降(P<0.05),SE略有升高。3种粘接剂相比,即刻及温度循环处理后SE粘接强度显著高于AP、GB组(P<0.05)。纳米渗漏结果显示一步法自酸蚀粘接剂界面渗漏比两步法更为显著。结论:温度循环实验可导致自酸蚀粘接剂界面的变化,表现为界面形态与粘接强度的变化。一步法自酸蚀粘接剂耐久性弱于两步法自酸蚀粘接剂。

关键词: 牙本质粘接剂, 酸蚀, 牙, 温度, 黏着性, 材料试验

Abstract: Objective:To investigate influence of thermalcycling on the bonding durability of two one-step products [Adper Prompt (AP) and G-bond (GB)] and one two-step self-etching adhesive [Clearfil SE bond (SE)] with dentin in vitro.  Methods:Forty-two extracted human molars were selected. The superficial dentin was exposed by grinding off the enamel. The teeth were randomly distributed into six groups with varied bonding protocols. The adhesives were applied to the dentin surface. Composite crowns were built up, then the samples were cut longitudinally into sticks with 1.0 mm×1.0 mm bon-ding area [for microtensile bond strength (MTBS) testing] or 1.0 mm thick slabs (for nanoleakage observation). Bonding performance was evaluated with or without thermalcyling. For the MTBS testing, the strength values were statistically analysed using One-Way ANOVA. Four slabs in each group were observed for nanoleakage by SEM with a backscattered electron detector.Results:Thermalcycling procedures affected MTBS. In the two onestep groups, the MTBS decreased significantly (P<0.05) after thermalcycling [AP group from (19.06±1.50) MPa to (12.62±2.10) MPa; GB group from (17.75±1.10) MPa to (6.24±0.42)MPa]. But in SE groups, MTBS did not significantly affect [(45.80±2.97) MPa compared with(40.60±5.76) MPa]. As a whole, one-step selfetching adhesives showed lower MTBS than two-step bonding system after aging.For AP and GB, continuous nanoleakage appearance was notable and more obvious than for SE. Conclusion:Thermalcycling can affect the bonding performance of self-etch adhesives including decrease of bond strength and nanoleakage pattern. One-step self-etch adhesives showed more obvious change compared with their two-step counterparts.

Key words: Dentin-bonding agents, Acid etching, dental, Temperature, Adhesiveness, Materials testing

[1] 薄士仕,高承志. 基于卷积神经网络实现锥形束CT牙齿分割及牙位标定[J]. 北京大学学报(医学版), 2024, 56(4): 735-740.
[2] 胡玉如,刘娟,李文静,赵亦兵,李启强,路瑞芳,孟焕新. Ⅲ期或Ⅳ期牙周炎患者龈沟液中有机酸浓度与牙周炎的关系[J]. 北京大学学报(医学版), 2024, 56(2): 332-337.
[3] 凌晓彤,屈留洋,郑丹妮,杨静,闫雪冰,柳登高,高岩. 牙源性钙化囊肿与牙源性钙化上皮瘤的三维影像特点[J]. 北京大学学报(医学版), 2024, 56(1): 131-137.
[4] 赵晓一,刘畅,钱锟,潘洁. 成熟恒牙牙髓切断术的疗效及影像学评价[J]. 北京大学学报(医学版), 2024, 56(1): 138-143.
[5] 郑佳佳,杨雪,温泉,付元,邵校,丁美丽. 生物活性陶瓷iRoot BP Plus®在儿童年轻恒前牙复杂冠折牙髓切断术中的应用[J]. 北京大学学报(医学版), 2024, 56(1): 179-184.
[6] 陈晨,梁宇红. 复杂根管上颌磨牙的根管治疗3例[J]. 北京大学学报(医学版), 2024, 56(1): 190-195.
[7] 张晗,秦亦瑄,韦帝远,韩劼. 牙周炎患者种植修复维护治疗依从性的影响因素[J]. 北京大学学报(医学版), 2024, 56(1): 39-44.
[8] 赵菡,卫彦,张学慧,杨小平,蔡晴,宁成云,徐明明,刘雯雯,黄颖,何颖,郭亚茹,江圣杰,白云洋,吴宇佳,郭雨思,郑晓娜,李文静,邓旭亮. 口腔硬组织修复材料仿生设计制备和临床转化[J]. 北京大学学报(医学版), 2024, 56(1): 4-8.
[9] 殳畅,韩烨,孙雨哲,杨再目,侯建霞. Ⅲ期牙周炎患者牙周基础治疗前后炎症性贫血相关指标的变化[J]. 北京大学学报(医学版), 2024, 56(1): 45-50.
[10] 王聪伟,高敏,于尧,章文博,彭歆. 游离腓骨瓣修复下颌骨缺损术后义齿修复的临床分析[J]. 北京大学学报(医学版), 2024, 56(1): 66-73.
[11] 李穗,马雯洁,王时敏,丁茜,孙瑶,张磊. 上前牙种植单冠修复体切导的数字化设计正确度[J]. 北京大学学报(医学版), 2024, 56(1): 81-87.
[12] 吴美辰,许桐楷,安伟,刘中宁,姜婷. 后牙高嵌体和贴面修复的4年临床随访[J]. 北京大学学报(医学版), 2024, 56(1): 88-92.
[13] 刘晓强,周寅. 牙种植同期植骨术围术期高血压的相关危险因素[J]. 北京大学学报(医学版), 2024, 56(1): 93-98.
[14] 段登辉,WANGHom-Lay,王恩博. 可吸收胶原膜在颊侧袋形瓣引导性骨再生手术中的作用: 一项回顾性影像学队列研究[J]. 北京大学学报(医学版), 2023, 55(6): 1097-1104.
[15] 许素环,王蓓蓓,庞秋颖,钟丽君,丁炎明,黄燕波,车新艳. 等体温膀胱冲洗对经尿道前列腺电切术患者干预效果的meta分析[J]. 北京大学学报(医学版), 2023, 55(4): 676-683.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!